clay(redirected from clay-like)
Also found in: Dictionary, Thesaurus.
Properties and Classification
Properties of the clays include plasticity, shrinkage under firing and under air drying, fineness of grain, color after firing, hardness, cohesion, and capacity of the surface to take decoration. On the basis of such qualities clays are variously divided into classes or groups; products are generally made from mixtures of clays and other substances. The purest clays are the china clays and kaolins. “Ball clay” is a name for a group of plastic, refractory (high-temperature) clays used with other clays to improve their plasticity and to increase their strength. Bentonites are clays composed of very fine particles derived usually from volcanic ash. They are composed chiefly of the hydrous magnesium-calcium-aluminum silicate called montmorillonite. See also fuller's earth.
Individual clay particles are always smaller than 0.004 mm. Clays often form colloidal suspensions when immersed in water, but the clay particles flocculate (clump) and settle quickly in saline water. Clays are easily molded into a form that they retain when dry, and they become hard and lose their plasticity when subjected to heat.
Clays are divided into two classes: residual clay, found in the place of origin, and transported clay, also known as sedimentary clay, removed from the place of origin by an agent of erosion and deposited in a new and possibly distant position. Residual clays are most commonly formed by surface weathering, which gives rise to clay in three ways—by the chemical decomposition of rocks, such as granite, containing silica and alumina; by the solution of rocks, such as limestone, containing clayey impurities, which, being insoluble, are deposited as clay; and by the disintegration and solution of shale. One of the commonest processes of clay formation is the chemical decomposition of feldspar.
Clay consists of a sheet of interconnected silicates combined with a second sheetlike grouping of metallic atoms, oxygen, and hydroxyl, forming a two-layer mineral such as kaolinite. Sometimes the latter sheetlike structure is found sandwiched between two silica sheets, forming a three-layer mineral such as vermiculite. In the lithification process, compacted clay layers can be transformed into shale. Under the intense heat and pressure that may develop in the layers, the shale can be metamorphosed into slate.
Clay as a Soil
See R. E. Grim, Clay Mineralogy (2d ed. 1968); R. W. Grimshaw, The Chemistry and Physics of Clays and Allied Ceramic Materials (4th ed. 1971).