noncombustibility

noncombustibility

That property of a material which enables it to withstand high temperature without ignition.
Mentioned in ?
References in periodicals archive ?
This study evaluated the combustion characteristics of PCM by means of cone calorimeter, noncombustibility, and flammability tests with varying experimental parameters such as polymer type, unit polymer content, polymer-cement ratio, and thickness of the specimen.
This study evaluated the combustion characteristics of PCMs by means of cone calorimeter, noncombustibility, and flammability tests with varying experimental parameters such as polymer type, unit polymer content, polymer-cement ratio, and thickness of the specimen [15, 16].
Flat specimens (100 x 100 x 10 (mm)) were used for the heat release rate tests and cylindrical specimens (diameter 44 x 50 (mm)) were used for the noncombustibility tests.
Noncombustibility tests were conducted according to ISO 1182 (reaction to fire tests for building products: noncombustibility test) [18].
As an important requirement in the noncombustibility test, the difference between the temperature of the incombustible material and the maximum temperature inside the furnace must be 20[degrees]C within 20 minutes after heating is commenced, and the average temperature 1 min after heating is ceased must be less than 20[degrees]C, with less than 30% weight loss of the specimen.
Behavior that tolerated fire close to the covering was induced by use of the name 'limestone,' which because it ends in '-stone' implies noncombustibility.
The article says that building materials having noncombustibility shall be those that are certified by the Minister of Land, Infrastructure, and Transport as having the properties mentioned in each of the following items (excluding number 3 in the case of those used for external finish of buildings) during the testing time of 20 minutes.
Asbestos has valuable properties such as noncombustibility and resistance to moisture, microorganisms, chemical attack, and decay.
However, these new gypsum panels do not comply with existing building code noncombustibility requirements.
Advantex EB8 yarn reportedly offers enhanced weaving processability and productivity levels, improved aesthetics, high dimensional stability, noncombustibility and fire resistance, as well as stronger reinforcement.
This standard is specifically structured toward testing for degrees of combustibility, and is designed to replace the older test for noncombustibility, ULC S114, equivalent to international ISO 1182 test.
Previously, ISO standards for the flammability area had covered only specialized fire performance areas such as fire resistance (ISO 834) and noncombustibility (ISO 1182) testing.