recrystallization annealing

recrystallization annealing

[rē‚krist·əl·ə′zā·shən ə‚nēl·iŋ]
(metallurgy)
Producing a new grain structure without phase change by annealing cold-worked metal.
References in periodicals archive ?
[1], who found that higher intermediate annealing temperature makes the microstructure become coarse before secondary cold rolling, which is a benefit to acquire Goss texture during recrystallization annealing. The effect of intermediate annealing process on microstructure and texture has been studied by Ju et al.
After that, the plate was cold rolled to a thickness of 0.68 mm and finally secondary cold rolled to a thickness of 0.27 mm after intermediate annealing; then, the primary recrystallization annealing was performed.
The current work investigated the effect of different intermediate annealing temperatures on the primary recrystallization textures under different primary recrystallization annealing temperatures which are 820[degrees]C and 850[degrees]C, respectively.
As presented in Figures 5(a) and 5(b), a higher primary recrystallization annealing temperature can reduce the content of low angle boundaries and increase the content of high angle boundaries at the same intermediate annealing temperature, which is conducive to the abnormal growth of Goss grains during the secondary recrystallization [10].
(4.) Suzuki, Y, Yamashita, T, Sugimoto, Y, et al., "Thermodynamic Analysis of Selective Oxidation Behavior of Si and Mn-Added Steel During Recrystallization Annealing." ISU Int., 49 (4) 564-573 (2009).
(36.) Drillet, P, Zermout, Z, Bouleau, D, et al., "Selective Oxidation of IFTi Stabilized Steels During Recrystallization Annealing, and Steel/Zn Reactivity." Galvatech'01: 5th Internationa!
Specific topics covered include structural and electron-hopping studies of Pr- and Nd-substituted manganites, recrystallization annealing of cold-rolled ferritic steel containing silicon, quantitative concepts for morphological stability analysis of solid/liquid interface in rapid solidification of dilute binary alloys, and studies of the spin Hamiltonian parameters for NiX2 and CdX2:Ni2+.